| Brand Name: | DLX |
| Model Number: | Ni201 (UNS N02201) Pure Nickel Rod |
| MOQ: | 10KG |
| Price: | Ni201 USD 350-390/kg; Ni200 USD 340-380/kg (FOB, by grade) |
| Supply Ability: | 10,000 t/yr (total plant capacity) |
Machined parts inherit the rod they are cut from: Nickel 201 rod in 8, 10, 12 and 20 mm sizes has to be consistent from the first cut to the last. Produced from Ni201 (UNS N02201, ≥99.0% Ni) with a clean, machinable structure and low electrical resistivity of 0.096 μΩ·m, our rod is supplied with custom diameters confirmed against your drawing — 10 kg MOQ, 3-7 day delivery for small lots, 7-15 days for standard production, from our ISO 9001 certified nickel-only line.
Rod is produced in 8 mm, 10 mm, 12 mm and 20 mm diameters as specified, with custom diameters and lengths per drawing. Diameter tolerance and length are confirmed before production and locked in the batch record.
Rod diameters are chosen for the finished part: 8-20 mm covers common turned and milled components, with machining allowance confirmed against the drawing. Custom diameters and lengths are produced per order.
Ni201 (≥99.0% Ni, ≤0.02% C) is specified for machined parts that see elevated temperature in service; Ni200 (≥99.2% Ni) is the standard grade for general machining. Grade selection is confirmed against the application.
Rod is supplied from verified melts with per-batch composition analysis, so every part machined from the bar inherits the same chemistry — no surprise inclusions or property drift along the length.
| Item | Detail |
|---|---|
| Product standards | ASTM B160 (nickel and nickel alloy rod and bar); GB/T 4435-2010 (nickel and nickel alloy rods) |
| Mill documentation | EN 10204 3.1 mill test certificates, batch composition and dimensional records |
| Management system | ISO 9001 certified; SGS audited |
| Traceability | Batch numbers tied to the drawing from melt to shipment |
| Grade | Ni Content | Best Application | Reference Price (FOB, USD/kg) |
|---|---|---|---|
| N4 (NP1) | ≥99.9% | Vacuum electronics | 420-480 |
| Ni201 | ≥99.0% | High-temp service | 350-390 |
| Ni200 | ≥99.2% | Battery, chemical | 340-380 |
| N6 (NP2) | ≥99.5% | Industrial corrosion | 300-340 |
The bands above are indicative for standard sizes; rod pricing follows grade, diameter, length and quantity, with custom sizes quoted per drawing.
| Element (wt%) | N4 | N6 | Ni201 | Ni200 |
|---|---|---|---|---|
| Ni | — | — | ≥99.0 | ≥99.2 |
| Ni+Co | 99.9 | 99.5 | — | — |
| Cu | ≤0.015 | 0.1 | ≤0.25 | ≤0.25 |
| Si | ≤0.03 | 0.1 | ≤0.35 | ≤0.35 |
| Mn | ≤0.002 | 0.05 | ≤0.35 | ≤0.35 |
| C | ≤0.01 | 0.1 | ≤0.02 | ≤0.15 |
| Mg | ≤0.01 | 0.1 | — | — |
| S | ≤0.001 | 0.005 | ≤0.01 | ≤0.01 |
| P | ≤0.001 | 0.002 | — | — |
| Fe | ≤0.04 | 0.1 | ≤0.4 | ≤0.4 |
| Property | Value |
|---|---|
| Density | 8.908 g/cm³ |
| Melting Point | 1435-1446 °C |
| Curie Temperature | 358 °C |
| Tensile Strength | ≥462 MPa (annealed) |
| Elongation | ≥35% (annealed) |
| Hardness | 90-120 HB |
| Electrical Resistivity | 0.096 μΩ·m (20 °C) |
| Thermal Conductivity (Ni200) | 70.2 W/m·K |
| Item | Detail |
|---|---|
| Diameter | 8 mm / 10 mm / 12 mm / 20 mm |
| Form | Rod (round bar) |
| Custom Sizes | Per drawing (diameter, length per drawing) |
| Tolerance | Per drawing, locked in batch record |
| Condition | Annealed (soft) standard |
| Surface | Clean, smooth, scale-free |
| Applicable Standards | ASTM B160; GB/T 4435-2010 |
Quality control starts at the melt: raw material composition is verified against UNS N02201 before forming, then every batch is gauged for diameter, length and surface condition. Batch records link each order back to the melt, and EN 10204 3.1 mill test certificates ship with every consignment.
Material data on this page follows ASTM B160 and GB/T 4435-2010; corrosion and application guidance references nickel industry literature (Nickel Institute; ASM Specialty Handbook: Nickel, Cobalt, and Their Alloys). Batch-level composition and geometry are verified against mill test certificates (EN 10204 3.1) and in-house inspection records.
Rod is bundled with protective wrapping, packed in export wooden cases. Documentation — mill test certificates, batch records and packing lists — accompanies every order. Small lots ship in 3-7 days; standard production in 7-15 days from confirmed drawing.
Every machined part starts as a bar, and the bar decides the part's tolerance from the first cut. DLX Alloy has run a nickel-only line since 2002 — 12,000 m² of floor space, 10,000 t/yr total capacity, ISO 9001 certified and SGS audited — supplying nickel rod in Ni201 and Ni200 with per-batch composition analysis and EN 10204 3.1 mill test certificates on every bundle.
Submit your drawing and quantity for a confirmed quote — grade, diameter and lead time confirmed before production.
8 mm, 10 mm, 12 mm and 20 mm as specified; custom diameters and lengths are produced per drawing.
Yes. Consistent chemistry and structure support turning, milling and drilling; the annealed condition gives the soft state most machining programs expect.
Ni201 (≥99.0% Ni, low carbon) for parts that see elevated temperature; Ni200 (≥99.2% Ni) for general machining.
10 kg; sample and trial quantities can be discussed per request.
EN 10204 3.1 mill test certificates, batch composition and dimensional records, ISO 9001/SGS certificates and packing list.
english
français
Deutsch
Italiano
Русский
Español
português
Nederlandse
ελληνικά
日本語
한국
中文
العربية
हिन्दी
Türkçe
indonesia
tiếng Việt
ไทย
বাংলা
فارسی
polski