700 MPA Hard 0Cr21Al4 Resistance Heating Strip FCHW 2
Contact me for free samples and coupons.
WhatsApp:0086 18588475571
WeChat: 0086 18588475571
skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xProduct Details
| Material | Ferrous Chromium Aluminum | Nickel(Min) | Cr 17 Al 4 |
|---|---|---|---|
| Resistivity | 1.23+/-0.05 | Tensile Strength | 700MPA |
| Elongtation | ≥12% | Application | Heating, Resistivity |
| Condition | Hard / Soft | Sureface | Bright, Oxided, Acide |
| Delivery Time | 7-20 Days | Maximum Temperature | 1100℃ |
| Melting Point | 1400℃ | Name | Resistance Heating Strip |
| Highlight | 700 MPA FCHW 2,0Cr21Al4 Fecral,Resistance Heating Strip FCHW 2 |
||
Product Description
- FeCrAl Series
FeCrAl alloy has the characteristic of high resistivity, low temperature resistance coefficient, high operating temperature, good anti-oxidation and anti-corrosion under high temperature.
It is widely used in industrial furnace, household appliances, metallurgy, machinery, aircraft, automotive, military and other industries producing heating elements and resistance elements.
Common Name: OhmAlloy123,FCHW-2
0Cr21Al4 resistance heating strip.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
|