Product Details
Place of Origin: China
Brand Name: DLX
Model Number: 0Cr27Al7Mo2
Payment & Shipping Terms
Minimum Order Quantity: 5
Packaging Details: Spool package with Carton box, Coil package with polybag
Delivery Time: 5-21 days
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: 300 tons per month
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.53+/-0.05 |
Tensile Strength: |
680-830MPA |
Elongtation: |
≥10% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1400℃ |
Melting Point: |
1520℃ |
Name: |
FeCrAl Alloy 0Cr27Al7Mo2 Strip |
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.53+/-0.05 |
Tensile Strength: |
680-830MPA |
Elongtation: |
≥10% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1400℃ |
Melting Point: |
1520℃ |
Name: |
FeCrAl Alloy 0Cr27Al7Mo2 Strip |
FeCrAl Alloy 0Cr27Al7Mo2 has great resistance to oxidation and corrosion in sulfur based conditions. Very high service temperature and prolong life. Due to its higher electric resistivity, lower density and superior heat resistance as compare to austenitic stainless steels, it is an ideal material for a variety of industrial heating operations. Large magnitudes of chromium and aluminum enhance resistance to oxidation and contamination.
Iron-Chromium-Alloy (FeCrAl Alloy) heating resistance alloys have high temperature creeping strength, good emissivity, nominal thermal expansion, small elastic modulus and excellent resistance to scaling and thermal shock. Moreover, good strength and ductile nature at the formation temperatures.
Industrial infrared heaters, radiators, coils for air heaters, furnace parts, space heating, fiber shielding material in ceramic glass top temperature, ceramic elements for panel heaters, heating plates, cartridge heaters, hair dryers, mica elements for irons, heating wires or cables.
FeCrAl Alloy resistance heating materials are employed in the various applications from household devices to heavy industrial process heating equipments and furnaces. In the industrial heating operations, these are used as open heating coils of resistance wire installed with ceramic bushing in a metal frame or metal sheath elements that are made of helical coil of resistance wire. Normally, heating materials perform at the extremely high temperatures up to 1300oC in the metal processing industrial furnaces.
| FeCrAl Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
|
|
||
|
||
|
||
|
||
|
||