780 MPA 0Cr25Al5 1.4765 Nickel Chromium Iron Alloy
Product Details:
| Place of Origin: | China |
| Brand Name: | DLX |
| Model Number: | 0Cr25Al5 |
Payment & Shipping Terms:
| Minimum Order Quantity: | 5 |
|---|---|
| Packaging Details: | Spool package with Carton box, Coil package with polybag |
| Delivery Time: | 5-21 days |
| Payment Terms: | L/C, T/T, Western Union, MoneyGram |
| Supply Ability: | 300 tons per month |
|
Detail Information |
|||
| Material: | Ferrous Chromium Aluminum | Resistivity: | 1.42+/-0.05 |
|---|---|---|---|
| Tensile Strength: | 630-780MPA | Elongtation: | ≥12% |
| Application: | Heating, Resistivity | Condition: | Hard / Soft |
| Sureface: | Bright, Oxided, Acide | Delivery Time: | 7-20 Days |
| Maximum Temperature: | 1250℃ | Melting Point: | 1500℃ |
| Name: | Resistance Heating Flat Wire | ||
| High Light: | 780 MPA Nickel Chromium Iron Alloy,0Cr25Al5 Aluchrom O,1.4765 Nickel Chromium Iron Alloy |
||
Product Description
- FeCrAl Series
Iron-Chrome-Aluminum FeCrAl 0Cr25Al5 resistance heating alloy has high maximum service temperature in air up to 1250oC. Longer life permits large surface stress to be applied on the alloy. Lighter weight makes it a more economical resistance heating material than Nichrome. The electric resistivty remains almost constant with varying temperatures. Good yield strength and aging resistance. Outstanding form stability. Greater heat resistance than austenitic stainless steels therefore it is commonly used in the heating applications.
FeCrAl 0Cr25Al5 resistance heating alloy Applications
Infrared heaters, heating plates, irons, ceramic heaters & pots, fan heaters, quartz tube heaters, toasters, ovens, storage heaters, bead insulated coils, open coil components, hot air guns, convection heaters, radiators, industrial furnaces for heat processing, metal sheath tubular elements, suspended coil elements for air heaters
Heanjia Super-Metals manufactures resistance heating elements for the wide range of applications varying from industrial furnaces to domestic appliances.
Industrial Nomenclatures: UNS K92500, 1.4765
Common Name:Aluchrom-O,OhmAlloy142B
0Cr25Al5 Ferrous Chromium Aluminum FeCrAl resistance heating flat wire.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
|
- The Form we could offer
|
||
|
||
|
||
|
||
|
||