Product Details
Place of Origin: China Jiangsu
Brand Name: DLX
Certification: CE,ROHS
Model Number: 0Cr27Al7Mo2
Payment & Shipping Terms
Minimum Order Quantity: 5
Price: Negotiable
Packaging Details: Spool package with Carton box, Coil package with polybag
Delivery Time: 5-20 Days
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: 500 tons per month
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.53+/-0.05 |
Tensile Strength: |
680-830MPA |
Elongtation: |
≥10% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1400℃ |
Melting Point: |
1520℃ |
Name: |
FeCrAl Resistance Heating Wire |
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.53+/-0.05 |
Tensile Strength: |
680-830MPA |
Elongtation: |
≥10% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1400℃ |
Melting Point: |
1520℃ |
Name: |
FeCrAl Resistance Heating Wire |
0Cr27Al7Mo2 is an iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1400°C (2552°F). The alloy with the characteristics of high resistivity, low temperature coefficient of electric resistance, high operating temperature, good oxidation resistance under high temperature. It can equal to APM.
0Cr27Al7Mo2 resistance wire is commonly used in electric heaters such as electric kettles, water dispensers, and electric pots. They use the heat generated by the resistance wire to heat water to the desired temperature, providing hot water and beverages for daily household needs.
In ovens and microwaves, 0Cr27Al7Mo2 resistance wire serves as a heating element, responsible for heating food to the desired temperature. They can quickly and evenly transfer heat to the food, ensuring effective heating and better cooking results.
Electric blankets and heating pads use the heat generated by 0Cr27Al7Mo2 resistance wire to provide users with a warm and comfortable sleeping environment. They can evenly heat the bed surface, alleviate discomfort from cold weather, and improve sleep quality.
In hair dryers and electric irons, 0Cr27Al7Mo2 resistance wire is used as a heating element to accelerate airflow or provide heat, facilitating quick hair drying or clothes ironing.
Water heaters and boilers commonly use 0Cr27Al7Mo2 resistance wire as a heating element to heat cold water to the desired temperature, providing hot water supply for bathing and cleaning needs.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Magnetic |
|
|
||
|
||
|
||
|
||
|
||