Product Details
Place of Origin: China Jiangsu
Brand Name: DLX
Certification: CE,ROHS
Model Number: 0Cr27Al7Mo2
Payment & Shipping Terms
Minimum Order Quantity: 5
Price: Negotiable
Packaging Details: Spool package with Carton box, Coil package with polybag
Delivery Time: 5-20 Days
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: 500 tons per month
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.53+/-0.05 |
Tensile Strength: |
680-830MPA |
Elongtation: |
≥10% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1400℃ |
Melting Point: |
1520℃ |
Name: |
FeCrAl Resistance Heating Wire |
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.53+/-0.05 |
Tensile Strength: |
680-830MPA |
Elongtation: |
≥10% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1400℃ |
Melting Point: |
1520℃ |
Name: |
FeCrAl Resistance Heating Wire |
0Cr27Al7Mo2 is an iron-chromium-aluminium alloy (FeCrAl alloy) for use at temperatures up to 1400°C (2552°F). The alloy with the characteristics of high resistivity, low temperature coefficient of electric resistance, high operating temperature, good oxidation resistance under high temperature. It can equal to APM.
In the industrial field, electric furnaces are widely used in various heating processes, such as metal heating, glass manufacturing, ceramic sintering, etc. 0Cr27Al7Mo2 resistance wire, as the heating element of electric furnaces, can operate stably in high-temperature environments, providing the required heating power to efficiently heat the workpiece.
Resistance heaters are a common type of heating device that uses the heat generated by passing current through resistance wire to heat the workpiece. 0Cr27Al7Mo2 resistance wire is commonly used as the heating element of resistance heaters due to its excellent resistance characteristics and high temperature resistance, and it can be widely used in industrial heating, laboratory research, and other fields.
Electric heating tubes are devices that use the heat generated by resistance wire to heat fluids or gases. 0Cr27Al7Mo2 resistance wire is made into the heating core of electric heating tubes, providing stable heating effects and widely used in household and industrial equipment such as electric water heaters and electric fans.
Electric heating is a common heating method in the process of metal smelting. 0Cr27Al7Mo2 resistance wire is used as the electric heating element of melting furnaces, providing high-temperature and high-power heating effects to efficiently carry out metal smelting.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Magnetic |
|
|
||
|
||
|
||
|
||
|
||