Product Details
Place of Origin: China
Brand Name: DLX
Model Number: 0Cr21Al6
Payment & Shipping Terms
Minimum Order Quantity: 5
Packaging Details: Spool package with Carton box, Coil package with polybag
Delivery Time: 5-21 days
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: 300 tons per month
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.42+/-0.05 |
Tensile Strength: |
630-780MPA |
Elongtation: |
≥12% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1250℃ |
Melting Point: |
1500℃ |
Name: |
Resistance Heating Wire |
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.42+/-0.05 |
Tensile Strength: |
630-780MPA |
Elongtation: |
≥12% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1250℃ |
Melting Point: |
1500℃ |
Name: |
Resistance Heating Wire |
0Cr21Al6 resistance wire is widely used in industrial and electrical fields, mainly in heating elements, resistors, thermocouples, and more.
0Cr21Al6 resistance wire is commonly used in resistors. Resistors are electronic components used to limit current or adjust voltage in circuits.
Due to its excellent high-temperature stability and oxidation resistance, 0Cr21Al6 resistance wire can operate stably in high-temperature environments.
The temperature coefficient of the 0Cr21Al6 resistance wire is low, allowing it to maintain a relatively stable resistance value over a wide temperature range.
Heating elements in injection molding machine heaters often utilize 0Cr21Al6 resistance wire to heat and maintain the flow state of plastics during the injection molding process.
This resistance wire can achieve high resistance values, making it suitable for circuit designs that require high resistance.
0Cr21Al6 resistance wire has good wear resistance and corrosion resistance, thus offering a longer lifespan.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Magnetic |
|
|
||
|
||
|
||
|
||
|
||