Product Details
Place of Origin: China
Brand Name: DLX
Model Number: 0Cr21Al6
Payment & Shipping Terms
Minimum Order Quantity: 5
Packaging Details: Spool package with Carton box, Coil package with polybag
Delivery Time: 5-21 days
Payment Terms: L/C, T/T, Western Union, MoneyGram
Supply Ability: 300 tons per month
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.42+/-0.05 |
Tensile Strength: |
630-780MPA |
Elongtation: |
≥12% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1250℃ |
Melting Point: |
1500℃ |
Name: |
Resistance Heating Wire |
Material: |
Ferrous Chromium Aluminum |
Resistivity: |
1.42+/-0.05 |
Tensile Strength: |
630-780MPA |
Elongtation: |
≥12% |
Application: |
Heating, Resistivity |
Condition: |
Hard / Soft |
Sureface: |
Bright, Oxided, Acide |
Delivery Time: |
7-20 Days |
Maximum Temperature: |
1250℃ |
Melting Point: |
1500℃ |
Name: |
Resistance Heating Wire |
0Cr21Al6 resistance wire is widely used in industrial and electrical fields, mainly in heating elements, resistors, thermocouples, and more.
0Cr21Al6 resistance wire is a commonly used electric heating alloy material with various applications in household appliances.
0Cr21Al6 resistance wire is widely used as heating elements in ovens and oven light bulbs. They generate high temperatures inside the oven for baking food and provide illumination.
In dryers, 0Cr21Al6 resistance wire serves as heating elements to help heat and dry clothes, bedding, etc.
Heating elements inside electric kettles and coffee machines often utilize 0Cr21Al6 resistance wire to quickly heat water or coffee, providing users with hot beverages.
In household water heaters, 0Cr21Al6 resistance wire is used as heating elements to help heat water for bathing, washing, etc.
Electric blankets are bedding items used to provide extra warmth, and the heating elements inside them typically employ 0Cr21Al6 resistance wire to maintain a warm and comfortable bed.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Magnetic |
|
|
||
|
||
|
||
|
||
|
||