FECRAL Alloy 16 SWG 0Cr21Al4 Resistance Wire For Household Appliances
Contact me for free samples and coupons.
WhatsApp:0086 18588475571
WeChat: 0086 18588475571
skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xDelivery Time | 7-20 Days | Material | Ferrous Chromium Aluminum |
---|---|---|---|
Resistivity | 1.23+/-0.05 | Tensile Strength | 700MPA |
Elongtation | ≥12% | Application | Heating, Resistivity |
Condition | Hard / Soft | Sureface | Bright, Oxided, Acide |
Maximum Temperature | 1100℃ | Melting Point | 1400℃ |
Name | Resistance Heating Wire |
- FeCrAl Series
0Cr21Al4 resistance wire is a type of iron chromium aluminum alloy resistance wire, which has good high-temperature stability and oxidation resistance, and is therefore widely used in many fields.
By being used in household appliances, 0Cr21Al4 resistance wire provides users with efficient and stable heating solutions, improving the performance and user experience of household appliances.
- Oven
0Cr21Al4 resistance wire is used as a heating element in ovens to provide stable heating, ensuring even heating for better cooking results.
- Water heater
0Cr21Al4 resistance wire is used as a heating element in water heaters to quickly heat water and maintain a constant temperature, providing users with comfortable hot water.
- Toaster oven
0Cr21Al4 resistance wire is used as a heating element in toaster ovens to quickly heat up, making bread golden and crispy, providing a delicious breakfast option.
- Coffee machine
0Cr21Al4 resistance wire is used as a heating element in coffee machines to quickly heat water, allowing coffee to be brewed in a short time while preserving its aroma and flavor.
- Induction cooktop
0Cr21Al4 resistance wire is used as a heating element in induction cooktops to provide efficient heating, quickly heating the cookware to the desired temperature, achieving precise cooking.
- Ferrous Chromium Aluminum alloy performance tables
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Magnetic |
- The Form we could offer