Nichrome Cr15Ni60 Chrome Nickel Wire High Temperature Resistance Alloy Wire

Contact me for free samples and coupons.
WhatsApp:0086 18588475571
WeChat: 0086 18588475571
skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xMaterial | Nickel, Chromium | Nickel(Min) | 55% |
---|---|---|---|
Resistivity | 1.12+/-0.05 | Tensile Strength | 637MPA |
Elongtation | ≥20% | Application | Heating, Resistivity |
Condition | Hard / Soft | Sureface | Bright, Oxided, Acide |
Delivery Time | 7-20 Days | Name | Cr15Ni60 |
Highlight | Cr15Ni60 Chrome Nickel Wire,637 MPA Chrome Nickel Wire,Nichrome Resistance Alloy Wire |
Nichrome Cr15Ni60 chrome nickel wire high temperature resistance alloy wire resistance
- NiCr Series
The Cr15Ni60 resistance alloy is composed of nickel-chromium alloy, which has high resistivity, good oxidation resistance and very stability. The maximum applicable temperature is up to 1200 degrees, and it has a longer service life than iron, chromium and aluminum.The alloy is widely used in household components, industrial furnaces and various resistance components, such as wirewound resistors, sheet metal resistors, hair dryers, electric furnaces, iron smelting, ovens, and even electronic cigarettes.
- Nickel-chromium alloy performance tables
Performance material | Cr10Ni90 | Cr20Ni80 | Cr30Ni70 | Cr15Ni60 | Cr20Ni35 | Cr20Ni30 | |
Composition | Ni | 90 | Rest | Rest | 55.0~61.0 | 34.0~37.0 | 30.0~34.0 |
Cr | 10 | 20.0~23.0 | 28.0~31.0 | 15.0~18.0 | 18.0~21.0 | 18.0~21.0 | |
Fe | ≤1.0 | ≤1.0 | Rest | Rest | Rest | ||
Maximum temperature℃ | 1300 | 1200 | 1250 | 1150 | 1100 | 1100 | |
Meltiing point ℃ | 1400 | 1400 | 1380 | 1390 | 1390 | 1390 | |
Density g/cm3 | 8.7 | 8.4 | 8.1 | 8.2 | 7.9 | 7.9 | |
Resistivity | 1.09±0.05 | 1.18±0.05 | 1.12±0.05 | 1.00±0.05 | 1.04±0.05 | ||
μΩ·m,20℃ | |||||||
Elongation at rupture | ≥20 | ≥20 | ≥20 | ≥20 | ≥20 | ≥20 | |
Specific heat | 0.44 | 0.461 | 0.494 | 0.5 | 0.5 | ||
J/g.℃ | |||||||
Thermal conductivity | 60.3 | 45.2 | 45.2 | 43.8 | 43.8 | ||
KJ/m.h℃ | |||||||
Coefficient of lines expansion | 18 | 17 | 17 | 19 | 19 | ||
a×10-6/ | |||||||
(20~1000℃) | |||||||
Micrographic structure | Austenite | Austenite | Austenite | Austenite | Austenite | ||
Magnetic properties | Nonmagnetic | Nonmagnetic | Nonmagnetic | Weak magnetic | Weak magnetic |