Ni60Cr15 Tubular Strip Nickel Chromium Iron Alloy

Contact me for free samples and coupons.
WhatsApp:0086 18588475571
WeChat: 0086 18588475571
skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xMaterial | Nickel, Chromium | Nickel(Min) | 55% |
---|---|---|---|
Resistivity | 1.12+/-0.05 | Tensile Strength | 637MPA |
Elongtation | ≥20% | Application | Heating, Resistivity |
Condition | Hard / Soft | Sureface | Bright, Oxided, Acide |
Delivery Time | 7-20 Days | Name | Resistance Heating Strip |
Highlight | Ni60Cr15 Nickel Chromium Iron Alloy,Tubular Nickel Chromium,Strip Nickel Chromium Iron Alloy |
- NiCr Series
Ni60Cr15 NiCr strip is high resistitivity alloy, it is suitable for temperature applications up to 1150°C. This alloy is characterized by high resistivity, good oxidation resistance, very good form stability, good ductility after use and excellent weldabilit. Ni60Cr15 is used for electric heating elements in domestic and industrial appliances. Typical applications: potentiometers, heavy-duty resistors, tubular heaters, electric furnaces, grills, hot plates, toasters, storage heaters, fan heaters, hand dryers, etc.
Common Name:Chromel C, Nikrothal 60, N6, HAI-NiCr 60, Tophet C, Resistohm 60, Cronifer II,Electroloy, Nichrome, Alloy C, Alloy 675,Nikrothal 6, MWS-675, Stablohm 675,NiCrC
Ni60Cr15 Nickel-Chromium Nickel alloy resistance heating flat wire, ribbon.
- Nickel-chromium alloy performance tables
Performance material | Cr10Ni90 | Cr20Ni80 | Cr30Ni70 | Cr15Ni60 | Cr20Ni35 | Cr20Ni30 | |
Composition | Ni | 90 | Rest | Rest | 55.0~61.0 | 34.0~37.0 | 30.0~34.0 |
Cr | 10 | 20.0~23.0 | 28.0~31.0 | 15.0~18.0 | 18.0~21.0 | 18.0~21.0 | |
Fe | ≤1.0 | ≤1.0 | Rest | Rest | Rest | ||
Maximum temperature℃ | 1300 | 1200 | 1250 | 1150 | 1100 | 1100 | |
Meltiing point ℃ | 1400 | 1400 | 1380 | 1390 | 1390 | 1390 | |
Density g/cm3 | 8.7 | 8.4 | 8.1 | 8.2 | 7.9 | 7.9 | |
Resistivity | 1.09±0.05 | 1.18±0.05 | 1.12±0.05 | 1.00±0.05 | 1.04±0.05 | ||
μΩ·m,20℃ | |||||||
Elongation at rupture | ≥20 | ≥20 | ≥20 | ≥20 | ≥20 | ≥20 | |
Specific heat | 0.44 | 0.461 | 0.494 | 0.5 | 0.5 | ||
J/g.℃ | |||||||
Thermal conductivity | 60.3 | 45.2 | 45.2 | 43.8 | 43.8 | ||
KJ/m.h℃ | |||||||
Coefficient of lines expansion | 18 | 17 | 17 | 19 | 19 | ||
a×10-6/ | |||||||
(20~1000℃) | |||||||
Micrographic structure | Austenite | Austenite | Austenite | Austenite | Austenite | ||
Magnetic properties | Nonmagnetic | Nonmagnetic | Nonmagnetic | Weak magnetic | Weak magnetic |