Corrosion Resistance FeCrAl Electric Resistance Wire 0Cr21Al6 For Thermocouple
Contact me for free samples and coupons.
WhatsApp:0086 18588475571
WeChat: 0086 18588475571
skype: sales10@aixton.com
If you have any concern, we provide 24-hour online help.
xDelivery Time | 7-20 Days | Material | Ferrous Chromium Aluminum |
---|---|---|---|
Resistivity | 1.42+/-0.05 | Tensile Strength | 630-780MPA |
Elongtation | ≥12% | Application | Heating, Resistivity |
Condition | Hard / Soft | Sureface | Bright, Oxided, Acide |
Maximum Temperature | 1250℃ | Melting Point | 1500℃ |
Name | Resistance Heating Wire |
- FeCrAl Series
0Cr21Al6 resistance wire is widely used in industrial and electrical fields, mainly in heating elements, resistors, thermocouples, and more.
0Cr21Al6 resistance wire is commonly used in thermocouples. Thermocouples are sensors used to measure temperature, based on the thermoelectric effect, which generates a voltage difference at the junction of two different metals to measure temperature.
- High Stability
Due to its excellent high-temperature stability and oxidation resistance, 0Cr21Al6 resistance wire can operate stably in high-temperature environments, providing accurate and reliable temperature measurements.
- Fast Response Time
0Cr21Al6 resistance wire has a fast response time, quickly sensing temperature changes and outputting corresponding voltage signals.
- Good Corrosion Resistance
This resistance wire has good corrosion resistance, capable of withstanding various chemical environments, ensuring long-term stable performance.
- Wide Applicability
0Cr21Al6 resistance wire has a wide temperature range, suitable for temperature measurement requirements in various industrial fields.
- Ferrous Chromium Aluminum alloy performance tables
Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | ||
Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |
Magnetic |
- The Form we could offer